Does anyone know if Argonite ArN2 is any good for TIG welding?? What about CO2?
Kindest Regards,
Richard.
...You can make it foolProof, but youll never make it Idiot Proof!...
|
|
|
|
|
big_wasa
|
| posted on 7/8/08 at 05:28 AM |
|
|
Nope its got to be Pure argon 
I tried to do a bit with argon /co2 as its all I had. You could do a little bit and then the weld pool would react and turn to aero bar
|
|
|
splitrivet
|
| posted on 7/8/08 at 06:51 AM |
|
|
I tried some it made me go all weak and listless oh sorry that was kryptonite.
Cheers,
Bob 
I used to be a Werewolf but I'm alright nowwoooooooooooooo
|
|
|
britishtrident
|
| posted on 8/8/08 at 06:20 PM |
|
|
Nitrogen in welds is bad news causes brittle fracture.---
|
|
|
Mark Allanson
|
| posted on 8/8/08 at 08:43 PM |
|
|
I suppose thats why they make low nitrogen welding rods