Alternative to welding - for those who want a choice
Terrapin_racing - 16/2/04 at 10:52 AM

Bronze welding is extremely easy to do. Far easier than MIG/TIG etc. This is not an inferior alternative. Indeed in a lot of respects bronze welding is far more superior in terms of strength and fatigue resistance. Used by Lotus, March, Williams etc. You must use a 9% nickel bronze rod (sifbronze number 2). The method is then just like brazing - but you build up a fillet around the joint. Use a good flux- sifbronze again. If anyone wants further details lease let me know.
The process is fully described in HSLC book.
cheers
Rob

http://7faq.com/owbase/ow.asp?NotesOnWelding

[Edited on 16/2/04 by Terrapin_racing]


David Jenkins - 16/2/04 at 12:26 PM

This was debated here quite a while ago - the MIG enthusiasts weren't convinced!

There is a 750 Club book that describes how that club formed. Part of that book discusses the use of brazing and the techniques used - quite different from welding. Not hard, just different.

The most interesting part is the intro, where one author describes a crash that the other author suffered: 100mph to 0 in about 6ft! He wasn't in very good condition, as you can imagine (he had a series of heart attacks from the impact against the harness) but he survived with few other physical injuries. This was in a brazed chassis, very similar to the Terrapin in fact.

David


Terrapin_racing - 16/2/04 at 12:59 PM

As an engineer with direct contact to industrial certified welding inspectors I chose bronze welding for it's toughness & resistance to cracking (MIG's form a very hard join!) - If you talk to the experts it is recognised that the parent metal will fail before the BW joint.
Incidentally, Allan Staniforth had a 80MPH crash at New Brighton Sprint (NW UK) and is still racing today. If anyone has seen the New Brighton sea wall you'll understand !! Rescued attachment NB.gif
Rescued attachment NB.gif


Alan B - 17/2/04 at 01:57 PM

Terrapin, while I would agree that bronze welding is not too difficult, certainly easier than TIG or gas welding.......I would have to disagree it was easier than MIG IMO

Neither would I ever claim bronze welding to be inferior (not that you are saying I'm saying that).....IMO, it is more difficult (somwhat) than MIG, and many orders of magnitude slower....also it does demand better joint fit-up (OK, good joint fit-up is desirable..)

Just my opinions to keep the thread alive...


Terrapin_racing - 17/2/04 at 03:30 PM

Well, i suppose the only answer is "if you can't do it yourself" employ someone who can!


Alan B - 17/2/04 at 03:37 PM

Not sure what you mean exactly, but I can bronze weld....just would not choose to build a a full car frame that way that's all...also, employing someone to weld your frame is very impractical.......you may as well just buy one....

Although in our cases that is not option either as neither of us are doing a "book" build.

I have said this before, but I found High Speed low cost more inspirational than the "book"


Terrapin_racing - 17/2/04 at 03:42 PM

Alan, apologies. It's not directed at you. Just a general comment to all those who want an alternative to welding because they are having difficulty mastering it.

Maybe I should say " If you can't do it yourself - then employ someone or buy it ready built"?

Or maybe - ask a mate

cheers
Rob


Alan B - 17/2/04 at 03:54 PM

No problem.

I like bronze welding and agree it is certainly no way inferior to other processes....bringing it back to everyone's attention is good for our combined knowledge pool.....I just got used to the ease and speed of MIG I guess....


Terrapin_racing - 17/2/04 at 04:06 PM

I use my MIG all the time, but bronze welded the chassis because it will take the stresses imparted in a lightweight space frame (I lifted it up single handed to put on the car roof to take to powdercoaters) chassis. Allan never experienced a joint failure - well if you read the book it says some where that he spent many hours watching the joints during his early days, he is now very complacent and accepts that they're fine.

My other car is entirely MIG welded!

I think it's in the background of some of my photos - The 1st crossflow engine (trophy winning) Midge - anyone remember them (and the Locust - a colleague built one at the same time)
I built it in the eighties and it's still concours! I remember ringing John Cowperthwaite (Moss cars, Monaco etc.)
about the errors on the Ford version plans and getting the response - "Oh - trial and error, your the first to build one"!

You guy's know the story!

[Edited on 17/2/04 by Terrapin_racing]


Alan B - 17/2/04 at 04:15 PM

I would certainly agree that BW scores higher the thinner you get.....burning through tubes is not an issue (within reason)

I'd say MIG starts to score when you hit 16g and thicker....

But we agree that both are perfectly acceptable processes for our tasks....

IIRC the Terrapin does use a lot of of lightweight 18g, 20g tubing?

Are you sticking with the mini power plant?...or using something more modern?


Terrapin_racing - 17/2/04 at 04:40 PM

Yes, the Terrapin uses a lot of 16g CDS round and 16g ERW tubing. I'm building to the original design using Mini powerplant (well Metro 1275MG A+ series engine + box with twin pin differential - to replace the standard diff which is the g/box week point)
A lot of Terrapins subsequently used Alfa, Rover V8? and then bike engines in the rear.
Cheers
Rob


Alan B - 17/2/04 at 05:20 PM

Rob,

Many years ago I was a member of Longton and district MC.....Keith Gowers was a member as was John Aldred (I think) both early "terrapinners".....do you know either?


sgraber - 17/2/04 at 07:24 PM

<cheerful banter mode>

Now don't chastise me for this question, but we are in Low Cost mode here. (I can imagine being told - "If you are building a car to the safest standards then cost is not an object..." Well sorry it is and I am currently Mig'ing along quite blissfully. with a little cheapo Mig welder.

</cheerful banter mode>

Excuse my ignorance (rookie builder mode). What is the expense of brazing vs mig welding? Averaged out over a typical frame say?

What would the average equipment cost and what are the material startup costs?


Alan B - 17/2/04 at 08:23 PM

Steve, a trip to Home depot and you could be bronze welding for 50 bucks..

A realistic decent setup maybe 300 dollars...

I believe there is certain stigma from both angles in this debate....

Traditionalists (Lotus, arch motors fans etc) say brazing/BW is the best and new- fangled MIG is cheap, corner cutting and inferior.....

MIG fans say that BW is outdated and new technology must be better...

Ok, I've exaggerated both viewpoints....but, IMO and sure Terrapin will agree is that both are good methods equally satisfactory when done properly....

Just because BW is long established and used by Caterham doesn't make it superior any more than TVR using MIG makes it superior....

I think it has a lot more to do tube thickness and speed than anything.


sgraber - 17/2/04 at 08:34 PM

but it looks so purdy!

Actually, I AM very interested in Bronze Welding and would like to at least try it sometime.

Question, Bronze welding doesn't inherently make for a lighter structure right?

However, the decreased chassis weight comes simply from the ability to use a thinner gauge tube because you aren't heat stressing (making brittle) the metal as much?

Sorry for the newbie style questions. :p You now realize that I have only ever MIG welded. (I am reading up on it now. Thanks for the link Rob.)


Alan B - 17/2/04 at 08:51 PM

Steve,

Yes decreased weight comes from the lighter tubing, but more because of better design taking bending loads out of tubes allowing thinner wall thickness....which in turn make BW more desirable.....

So I wouldn't say BW was inherently lighter just a better process for really thin tubes...which make up lighter frames..

Another factor (which Rob will correct me on if things have changed) is that BW clean up is nasty....lots hard glassy flux deposits to remove....sandblasting would be good I'd have thought...


Terrapin_racing - 18/2/04 at 09:56 AM

Well - Here I go....
To start bronze welding you need access to oxygen/acetylene gear. I have the middle range size bottle and rental is about £80 per annum in UK (excluding refill costs). The Sifbronze number 2 rods are about £30 for a 1kg box (hell of a lot of joints!) and the flux is about £8 for a large tub.
Bronze welding is a very similar practice to brazing but this type of rod allows you to build up a nice fillet around the joint. As Alan mentioned this allows you to use far lighter guage tubing and sheet. My chassis is primarily 16g with areas of 20g & 22g sheet and tube also.
Flux clean up is an issue. You need lots of 'elbow grease' hot water and a wire brush - or if you are not in a rush (and you live in UK!) you will find the glass like flux residue will turn to powder and fall away if left in a damp atmosphere for a few weeks. My chassis was then blast cleaned and powder coated at a reasonable cost (£140). If cost in not an issue you can purchase a gas fluxer for about £300 - this is a device installed in the acetylene line which used liquid flux (turns flame green) and leaves no residue.
A lot of the racing car manufacturers use these. Other points of really value - I have had bushes made from high tensile heat treatable steels EN24 etc (suspension lower ball joint tapers etc.) - you should not weld to these unless you have the facility to heat treat afterwards - the joints will be very brittle. Using Bronze welding for this is ideal as the effects are negligible if the joints are allowed to cool naturally (don't quench!).

On the issue of cost - someone said my car looks like it was all new bits so how could it be "High speed,low cost" - and how much did I spend?

Well, I gave a lengthy answer - but really - it is a case of how much do you want to spend? - I think you will all agree - you get what you pay for. A very acceptable car can be built on a budget but might not win any concours prizes. I did mention that you should never skimp on brakes, steering etc. Safety first guys - I once read an article where someone used second hand brake shoes from a breaker and cleaned them off with paint spirit prior to fitting - then wanted to know why the linings had broken away from the shoes (bonded, not riveted) - crazy!!! - fortunately he was lucky, the linings fouled up inside the drums and locked the wheels when they failed and nobody was hurt.

cheers
Rob

[Edited on 18/2/04 by Terrapin_racing]


dmottaway - 19/2/04 at 05:22 AM

anybody have an American equivalent to Sifbronze?

dave


Terrapin_racing - 19/2/04 at 09:22 AM

Here's the spec to ask for -


SIFBRONZE No. 2 (9% Ni)
BS: 1845 CZ8, 1453 C5
Nearest Equivalent Standards: DIN L-Ns, AWS RBCuZn-D

A high quality, free flowing rod containing 9% nickel which produces an exceptionally strong joint on cast iron, copper alloys, stainless and alloy steels. It has excellent wearing properties and is recommended for building worn components like gear teeth, bearings and valve seats, since it work hardens. The high strength characteristics make Sifbronze No.2 ideal for tubular structures, brazing cutting tips and as a general maintenance alloy. Use Sibronze or special purpose flux.
Melting point - 920-980 C
Tensile stength (N/mm2) 540
Hardness (BHN) 200
Typical composition:

48 Cu
10 Ni
0.3 Si
Balance Zn Rescued attachment sif.jpg
Rescued attachment sif.jpg


David Jenkins - 19/2/04 at 09:55 AM

I tried this with my basic TIG - it's bl**dy difficult!

Mind you, I was trying to braze a couple of bits of copper, and it was taking all the heat away from the joint area. I probably should have pre-heated the metal with propane before I started. Model steam engine boilers are often TIG'd, but they take the whole thing up to near red-hot before starting to braze (I'm talking about 30 - 50 lbs of copper here!)

David


Terrapin_racing - 19/2/04 at 10:04 AM

Yes, seen TIG used for this but.... Dave hit the nail on the head!
Problem is bringing the surrounding material up to temp so heat isn't drawn away. OK on small stuff.


David Jenkins - 19/2/04 at 10:50 AM

Also much easier on mild steel, which is a poor conductor of heat when compared to copper or brass - the heat stays near the joint long enough to allow the braze to flow.

David


stutz - 19/2/04 at 09:49 PM

Probably a silly question, but does anyone know if you can bronze weld stainless steel?

[Edited on 19/2/04 by stutz]


britishtrident - 13/3/04 at 07:59 AM

The arguments are finely balanced -- bronze welding has much in its favour -- the only major downside is the jig arangments need to be better to avoid building a twisted chassis.


Terrapin_racing - 15/3/04 at 09:44 AM

Stainless Steel - Yes!

SIFBRONZE No. 2 (9% Ni)
BS: 1845 CZ8, 1453 C5
Nearest Equivalent Standards: DIN L-Ns, AWS RBCuZn-D

A high quality, free flowing rod containing 9% nickel which produces an exceptionally strong joint on cast iron, copper alloys, stainless and alloy steels. It has excellent wearing properties and is recommended for building worn components like gear teeth, bearings and valve seats, since it work hardens. The high strength characteristics make Sifbronze No.2 ideal for tubular structures, brazing cutting tips and as a general maintenance alloy. Use Sibronze or special purpose flux.

To prevent any distortion the practice is to tack the chassis together and then bronze weld diametrically opposite joints
.The process is well decribed in Allan's book - HSLC


Mark Allanson - 15/3/04 at 10:17 AM

Vauxhall have recently put their approval on bronze welding for accident repairs. The reels of wire are £70 for 15kg, and you need to use pure argon as the shield, oh yes and a mig welder!


Terrapin_racing - 15/3/04 at 11:16 AM

Mmmmmmmmm ... I'd be interested in how this works? How is the repair metal "fluxed" or cleaned?
I've seen autofluxers but these are reliant on the flux being introduced into the acetylene stream. Argon alone will not clean the parent metals?
Got any more details?


Mark Allanson - 15/3/04 at 11:24 AM

We haven't used it yet, I suspect the wire is flux cored, hence the price. I will try to get a data sheet from our supplier, I will post it when I get it.


Terrapin_racing - 16/3/04 at 09:19 AM

Cheers Mark
Rob